Casting materials and their characteristics: Material: Hardness: Tensile strength: Czech norm: Composition: BRONZE 42 31 19 CuSn10 60 HB 220 MPa 42 31 23 CuSn12 80 HB 240 MPa 42 31 35 CuSn5Pb5Zn5 60 HB 150 MPa 42 31 37 CuSn8Pb3Zn6 65 HB 170 MPa 42 31 46 CuAl10Fe3Mn1,5 110-154 HB 400 MPa 42 31 48 CuAl10Ni2Mn1 130 HB 500 MPa We are able to produce a wide range of Cu alloys and then check the composition with SPECTROLAB M8. MEANS OF SHAPING AND PRODUCTION PARAMETERS: Means[...]

Casting materials and their characteristics: Casting material: GGK Hardness: 140 - 200 HB Tensile strength: 220 MPa PRODUCTION PARAMETERS: Material: GGK GGK Capacity: 24 chill machines 3 chill machines Casting weight: 0,4 kg - 10 kg up to 100 kg Max. dimensions of castings: 450 x 400 x 250 mm 1000 x 500 x 350 mm Efficient series: over 1000 pieces over 300 pieces CAPACITY: 350 tuns/monthly USAGE: For example: hydraulic and brake cylinders of motor vehicles, hydraulic and pneumatic[...]

Casting materials and their characteristics: Casting material: DIN 1725/226 DIN 1725/231 Hardness: 80 - 120 HBS 60 - 100 HBS Tensile strength: 240 - 310 N/mm2 200 - 220 N/mm2 The above mentioned materials represent our standard offer. Nevertheless we can cast also other materials, on the basis of an agreement with customers. PRODUCTION PARAMETERS: Casting weight: cca 0,005 - až 3 kg Surface of all castings in separating plane: 7,9 - 900 cm2 CAPACITY: 100 tuns/monthly USAGE: Especially[...]

Casting materials and their characteristics: Casting material: AlSi10MgMn AlCu4Si5Zn AlSi10CuMn AlZn10Si8Mg Hardness: 50 HB 70 HB 50 HB 100 HB Tensile strength: 137 MPa 140 MPa 120 MPa 167 MPa We are able to produce a wide range of Al alloys and then check the composition with SPECTROLAB M8. MEANS OF SHAPING AND PRODUCTION PARAMETERS: Means of shaping: A. manual B. mechanical Casting weight: 0,03 - 180 kg 0,03 - 15 kg Max. dimensions of castings: 1.500 x 1.500 mm (above standard[...]

Casting materials and their characteristics: Casting material: GG 15 GG 20 GG 25 Hardness: 140 - 200 HB 160 - 220 HB 180 - 240 HB Tensile strength: min. 150 MPa min. 200 MPa min. 250 MPa As regards mechanical shaping we offer standard accuracy from GTB 16. MEANS OF SHAPING AND PRODUCTION PARAMETERS: Means of shaping: A. manual B. mechanical Casting weight: 0,5 kg - 300 kg 0,3 kg - 25 kg Max. dimensions of castings: 1000 x 1000 x 500 mm 450 x 350 x 250 mm Efficient series: up[...]